17-7PH®, or Type 631 (UNS S17700), is a chromium-nickel-aluminum Precipitation Hardening Stainless Steel used in spring applications for numerous industries.
17-7PH® Overview
The alloy offers corrosion resistance comparable to 302, but it can achieve higher strength after precipitation hardening due to aluminum additions.
CWI is the leading producer of aerospace and commercial quality 17-7 spring wire in the U.S. and U.K.
CWI has decades of metallurgical experience with processing of 17-7 wire for spring applications. This research and process development optimizes the microstructural characteristics of our 17-7PH® spring wire to be fully compliant with AMS 5678G. CWI has established tight controls on several wire-drawing parameters and laboratory microstructure evaluations to ensure that the product is fully compliant to AMS 5678G.
17-7PH® 成分
| 类型 | C | 锰 | 磷 | 小号 | 硅 | 铬 | 你 | 莫 | 其他 |
|---|---|---|---|---|---|---|---|---|---|
| 17-7PH | 0.09 | 1.00 | 0.040 | 0.030 | 1.00 | 16.00 - 18.00 | 6.50 - 7.75 | - | - |
行业标准
合金的商业用途受行业标准的约束，例如：ASTM A313、EN 10270-3、ISO 6931。这些标准定义了标称出厂（条件 C）拉伸、CH900 拉伸和通过缠绕和卷取测试的延展性评估。
航空航天应用通过 AMS 5678G 提供，该标准通过对最终拉丝微观结构的额外鉴定测试进一步控制材料。
微观结构方面
17-7PH® 在固溶处理阶段以奥氏体结构开始。通过拉丝过程中的应变和冷加工，材料转变为马氏体结构，最终通过时效过程进一步强化，形成亚微观 NiAl（NiAl 和 Ni3Al）基析出物，增加材料的硬度和强度。
UNS S17700 – Al: 0.75-1.50, Cr: 16.0-18.0, Ni: 6.5-7.75
应用领域
17-7PH® 是一种理想的合金，适用于要求良好的成型性、高强度/硬度、良好的耐腐蚀性和热处理变形最小的应用。 17-7PH® 合金常用于汽车、航空航天、化学加工设备、石油和石油精炼设备以及食品加工设备。该合金还为温度高达 315°C (600°F) 的板簧提供了出色的性能。