CWI Generation4™ Stainless Steel and Nickel Welding wire alloys can be used with many different joint styles and welding processes. Once the weld joint style, the filler material, and the process has been identified, a proper welding procedure can be identified. The welding procedure chosen for Stainless Steel and Nickel welding depends upon the process to be used as well as the size and alloy of the actual consumable. The charts below provide detailed information on the voltage, amperage (current), and gas (atmosphere) to be used in TIG (Tungsten Inert Gas), MIG (Metal Inert Gas), and SAW (Submerged-Arc Welding) welding processed for the general alloys that we provide. If you have questions about selecting the right procedure, or about the recommended welding procedure for a specific CWI Generation4 ™ wire, contact a CWI material and applications expert today.
Empfohlene Schweißverfahren für Gen 4 Edelstahl-Schweißdraht
Verfahren | Durchmesser des Drahtes | Spannung (V) | Stromstärke (A) | Gas | |
---|---|---|---|---|---|
WIG | 0,035" | 0,9mm | 12-15 | 60-90 | 100% Argon |
0,045" | 1,1mm | 13-16 | 80-110 | 100% Argon | |
1/16" | 1,6mm | 14-18 | 90-130 | 100% Argon | |
3/32" | 2,4 mm | 15-20 | 120-175 | 100% Argon | |
1/8" | 3,2mm | 15-20 | 150-220 | 100% Argon | |
MIG | 0,030" | 0,8 mm | 24-28 | 140-180 | 99% Argon + 1% Sauerstoff -oder- 97% Argon + 3% CO2 |
0,035" | 0,9 mm | 26-29 | 160-210 | 99% Argon + 1% Sauerstoff -oder- 97% Argon + 3% CO2 | |
0,045" | 1,1 mm | 28-32 | 180-250 | 99% Argon + 1% Sauerstoff -oder- 97% Argon + 3% CO2 | |
SAH | 0,0625" | 1,6 mm | 29-33 | 200-280 | Geeignetes Flussmittel kann verwendet werden |
3/32" | 2,4 mm | 28-30 | 275-350 | Geeignetes Flussmittel kann verwendet werden | |
1/8" | 3,2 mm | 29-32 | 350-450 | Geeignetes Flussmittel kann verwendet werden | |
5/32" | 4,0 mm | 30-33 | 450-550 | Geeignetes Flussmittel kann verwendet werden |
Empfohlene Schweißverfahren für Edelstahl-Nickel-Schweißdraht der Generation 4
Verfahren | Durchmesser des Drahtes | Spannung (V) | Stromstärke (A) | Gas | |
---|---|---|---|---|---|
WIG | 0,035" | 0,9mm | 12-15 | 60-90 | 100% Argon |
0,045" | 1,1mm | 13-16 | 80-110 | 100% Argon | |
1/16" | 1,6mm | 14-18 | 90-130 | 100% Argon | |
3/32" | 2,4 mm | 15-20 | 120-175 | 100% Argon | |
1/8" | 3,2mm | 15-20 | 150-220 | 100% Argon | |
MIG | 0,035" | 0,9 mm | 26-29 | 150-190 | 75% Argon + 25% Helium |
0,045" | 1,2 mm | 28-32 | 180-220 | 75% Argon + 25% Helium | |
1/16" | 1,6 mm | 29-33 | 200-250 | 75% Argon + 25% Helium | |
SAH | 3/32" | 2,4 mm | 28-30 | 375-350 | Geeignetes Flussmittel kann verwendet werden |
1/8" | 3,2 mm | 29-32 | 350-450 | Geeignetes Flussmittel kann verwendet werden | |
5/32" | 4,0 mm | 30-33 | 400-550 | Geeignetes Flussmittel kann verwendet werden |