GEN 410NiMo Overview
GEN 410NiMo is primarily designed for welding ASTM CA6NM casting or similar materials. It may also be used
for welding light gauge 410, 410S, and 405 base materials. Final post‐weld heat treatment should not exceed 1150°F (620°C) as higher temperatures may result in re‐hardening.
AWS 化学成分（典型）
| %C | %Cr | %Ni | %Mo | %Mn |
|---|---|---|---|---|
|
0.06 max. 0.023 |
11.0 – 12.5 11.75 |
4.0 – 5.0 4.70 |
0.4 – 0.7 0.50 |
0.60 max. 0.46 |
| %Si | %P | %S | %Cu |
|---|---|---|---|
|
0.50 max. 0.44 |
0.03 max. 0.013 |
0.03 max. 0.002 |
0.75 max. 0.00 |
典型的焊接金属机械性能
| 抗拉强度 | 117,000 psi | 806 MPa |
| 屈服强度 | 92,000 psi | 634 MPa |
| Elongation (min.) | 20 % |
Typical Welding Parameters
| 过程 | Diameter | Voltage | Amperage | Gas/Flux |
|---|---|---|---|---|
| 氩弧焊 (GTAW) | 1/16” | 14 – 16 | 90 – 130 | 100% Ar |
| 3/32” | 15 – 20 | 120 – 180 | 100% Ar | |
| 米格 (GMAW) | .035” | 24 – 29 | 150 – 220 | 98%Ar – 2%O2 |
| .045” | 25 – 30 | 160 – 260 | 98%Ar – 2%O2 | |
| Sub Arc (SAW) | .093” | 28 – 32 | 250 – 450 | |
| .125” | 29 ‐ 34 | 300 – 500 |