GEN 310 Overview
GEN 310 is most often used to weld base metals of similar chemical composition in wrought or cast form. The
weld deposit is fully austenitic. Low heat input is recommended during welding.
ComposiciĂłn quĂmica de AWS (tĂpica)
| %C | %Cr | %Ni | %Mo | %Mn |
|---|---|---|---|---|
| 0.08 â 0.15 | 25.0 â 28.0 | 20.0 â 22.5 | 0.75 max | 1.0 â 2.5 |
| 0.12 | 25.9 | 20.7 | 0.09 | 1.65 |
| %Si | %P | %S | %Cu |
|---|---|---|---|
| 0.30 â 0.65 | 0.03 max | 0.03 max | 0.75 max |
| 0.40 | 0.001 | 0.012 | 0.063 |
Propiedades mecĂĄnicas tĂpicas del metal de soldadura
| Fuerza de TensiĂłn | 87,000 psi | 600 MPa |
| LĂmite elĂĄstico | 57,000 psi | 393 MPa |
| Alargamiento | 42 % |
Typical Welding Parameters
| Proceso | Diameter | Voltage | Amperage | Gas/Flux |
|---|---|---|---|---|
| TIG (GTAW) | 1/16â | 14 â 17 | 80 â 125 | 100% Ar |
| 3/32â | 15 â 20 | 125 â 200 | 100% Ar | |
| MIG (GMAW) | .035â | 23 â 29 | 150 â 250 | 98%Ar â 2%O2 |
| .045â | 24 â 30 | 160 â 270 | 98%Ar â 2%O2 | |
| Sub Arc (SAW) | .093â | 28 â 32 | 250 â 450 | |
| .125â | 29 â 34 | 300 â 500 |