GEN 316 Overview
GEN 316 is mainly used for welding molybdenum‐bearing stainless steel, such 316, 318 and 319. The presence of molybdenum provides improved resistance to pitting by corrosive liquids.
Chemische Zusammensetzung von AWS (typisch)
| %C | %Cr | %Ni | %Mo | %Mn |
|---|---|---|---|---|
| 0.08 max 0.043 |
18.0 – 20.0 18.35 |
11.0 – 14.0 11.3 |
2.0 – 3.0 2.11 |
1.0 – 2.5 1.76 |
| %Si | %P | %S | %Cu |
|---|---|---|---|
| 0.30 – 0.65 0,42 |
0.03 max 0,025 |
0.03 max 0,003 |
0.75 max 0.060 |
Typische mechanische Eigenschaften von Schweißgut
| Zerreißfestigkeit | 88,000 psi | 606 MPa |
| Ertragsstärke | 58,000 psi | 400 MPa |
| Verlängerung | 40 % |
Typical Welding Parameters
| Verfahren | Diameter | Voltage | Amperage | Gas/Flux |
|---|---|---|---|---|
| WIG (GTAW) | 1/16” (1.6 mm) | 14 – 17 | 90 – 130 | 100% Ar |
| 3/32” (2.4 mm) | 15 – 20 | 125 – 175 | 100% Ar | |
| MIG (GMAW) | .035” (0.9 mm) | 29 – 33 | 160 – 180 | |
| .045” (1.1 mm) | 29 – 33 | 180 – 220 | 98% Ar – 2% O2 | |
| .063” (1.6 mm) | 29 – 33 | 210 – 250 | ||
| Sub Arc (SAW) | .093” (2.4 mm) | 29 – 32 | 300 – 350 | |
| .125” (3.2 mm) | 29 – 32 | 400 – 550 | ||
| .156” (4.0 mm) | 29 – 32 | 500 – 650 |