GEN 309L Overview
GEN 309L is used to weld base metals of similar chemical composition in wrought or cast form. It is also suitable for joining dissimilar metals such as 18Cr‐8Ni stainless steel to mild steel. The low carbon content minimizes the possibility of carbide precipitation. GEN 309L is preferred over 309 for cladding over carbon or low alloy steels, as well as for dissimilar joints that undergo heat treatment.
Chemische Zusammensetzung von AWS (typisch)
| %C | %Cr | %Ni | %Mo | %Mn |
|---|---|---|---|---|
| 0.03 max 0,015 |
23.0 – 25.0 23.4 |
12.0 – 14.0 13.6 |
0.75 max 0,08 |
1.0 – 2.5 1,65 |
| %Si | %P | %S | %Cu |
|---|---|---|---|
| 0.30 – 0.65 0,04 |
0.03 max 0,02 |
0.03 max 0,01 |
0.75 max 0,06 |
Typische mechanische Eigenschaften von Schweißgut
| Zerreißfestigkeit | 87,000 psi | 600 MPa |
| Ertragsstärke | 59,000 psi | 406 MPa |
| Verlängerung | 35% |
Typical Welding Parameters
| Verfahren | Diameter | Voltage | Amperage | Gas/Flux |
|---|---|---|---|---|
| WIG (GTAW) | 1/16” (1.6 mm) | 14 – 18 | 90 – 130 | 100% Ar |
| WIG (GTAW) | 3/32” (2.4 mm) | 15 – 20 | 120 – 175 | 100% Ar |
| WIG (GTAW) | 1/8” (3.2 mm) | 16 – 20 | 150 – 220 | 100% Ar |
| MIG (GMAW) | .035” (0.9 mm) | 29 – 33 | 160 – 180 | 98% Ar – 2% O2 |
| MIG (GMAW) | .045” (1.1 mm) | 29 – 33 | 180 – 220 | |
| MIG (GMAW) | .063” (1.6 mm) | 29 – 33 | 210 – 250 | |
| Sub Arc (SAW) | .093” (2.4 mm) | 29 – 32 | 300 – 350 | |
| Sub Arc (SAW) | .125” (3.2 mm) | 29 – 32 | 400 – 550 | |
| Sub Arc (SAW) | .156” (4.0 mm) | 29 – 32 | 500 – 650 |