GEN 410NiMo Overview
GEN 410NiMo is primarily designed for welding ASTM CA6NM casting or similar materials. It may also be used
for welding light gauge 410, 410S, and 405 base materials. Final post‐weld heat treatment should not exceed 1150°F (620°C) as higher temperatures may result in re‐hardening.
Chemische Zusammensetzung von AWS (typisch)
| %C | %Cr | %Ni | %Mo | %Mn |
|---|---|---|---|---|
|
0.06 max. 0,023 |
11.0 – 12.5 11.75 |
4.0 – 5.0 4.70 |
0.4 – 0.7 0,50 |
0.60 max. 0,46 |
| %Si | %P | %S | %Cu |
|---|---|---|---|
|
0.50 max. 0,44 |
0.03 max. 0,013 |
0.03 max. 0,002 |
0.75 max. 0.00 |
Typische mechanische Eigenschaften von Schweißgut
| Zerreißfestigkeit | 117,000 psi | 806 MPa |
| Ertragsstärke | 92,000 psi | 634 MPa |
| Elongation (min.) | 20 % |
Typical Welding Parameters
| Verfahren | Diameter | Voltage | Amperage | Gas/Flux |
|---|---|---|---|---|
| WIG (GTAW) | 1/16” | 14 – 16 | 90 – 130 | 100% Ar |
| 3/32” | 15 – 20 | 120 – 180 | 100% Ar | |
| MIG (GMAW) | .035” | 24 – 29 | 150 – 220 | 98%Ar – 2%O2 |
| .045” | 25 – 30 | 160 – 260 | 98%Ar – 2%O2 | |
| Sub Arc (SAW) | .093” | 28 – 32 | 250 – 450 | |
| .125” | 29 ‐ 34 | 300 – 500 |